Material Specification:

 

Thermal Properties

 

Thermal Shock                                                                          2000 cycles (90 sec. at 75 °C, 90 sec. dwell, 90 sec. at 15°C) No effect

Should not be subjected to dry-ice or liquid nitrogen.

 

Smoke Emission                                                                         Low Smoke Emission – BS 6853 1999 App. D Clause d.8.4

Result – Ao(on) 8.75, Ao(off) 10.41

 

Flammability                                                                              Class 0 as classified by the current UK Building Regulations

 

Thermal Decomposition                                                           660° F (350° C)

 

Glass transition temperature (Tg)                                            250 - 265° F (120 - 130 °C)

 

Mechanical Properties

 

Tensile strength                                                                          12’330 psi (85 MPa)

 

Tensile Modulus                                                                          1’523’000 psi (10,500 MPa)

 

Elongation at break                                                                     0.8%

 

Flexural strength                                                                          16’000 psi (112 MPa)

 

Flexural Modulus                                                                         1’450’000 psi (10,000 MPa)

 

Compressive Strength                                                                  27500 psi (190 MPa)

 

Coefficient of linear thermal expansion                                     3.54 x 10-5

 

Water absorption - 24 hours at 23°C                                           0.06-0.068% by weight. Tested to ISO 62 (1980)

 

Radioactive Decontamination                                                       BS 4247 Part 1 Test A

 

Decontamination factor (geometric mean)                                 5598.0

 

Deviation factor                                                                                1.25

 

Ease of decontamination classification                                        Excellent

​

Chemical Resistance (24 hour spot test. Based on BS EN 438-2:1991)

 

Acetone                                                 Unaffected

Hydrogen Peroxide                             Unaffected

Acetonitrile                                           Unaffected

Methanol                                              Unaffected

Ammonium Hydroxide 28%              Unaffected

n-Butanol                                              Unaffected

Aqua regia                                             Unaffected

Nitric acid 70%                                      Very slight bleaching

Benzyl alcohol                                       Unaffected

Nitric acid - concentrated                    Slight yellowing

Chloroform                                            Unaffected

Nitric acid - fuming                               Attack and staining

Chloroform - 100%                               Unaffected

Perchloric acid – 0.1N                           Unaffected

Chromic acid pickle (*1)                       Unaffected

Phosphoric acid - concentrated          Unaffected

Dichloromethane                                  Surface attack

Potassium hydroxide pellet (*2)          Unaffected

Dimethylformamide                              Unaffected

Sodium hydroxide - 50%                       Unaffected

Ethyl acetate Unaffected                       Unaffected

Sodium hydroxide pellet (*2)               Unaffected

Formaldehyde 37%                                Unaffected

Sodium hypochlorite                             Unaffected

Hydrochloric acid - 30%                         Unaffected

Sulphuric acid - 70%                               Unaffected

Hydrochloric acid - concentrated         Unaffected

Sulphuric acid - concentrated               Surface Attack

Hydrofluoric acid - 40%                          Slight bleaching

 Xylene                                                      Unaffected

 

 

*1 - 72g/l chromium trioxide + 360g/l sulphuric acid Ɣ

*2 - Changes to concentrated solution, then partly carbonates.

*3 - Simmons may alter the specification of epoxy resin systems without notification

 

​